Physical Properties of Nickel Alloy 600 in the Annealed Condition at -20°F to +100°F
| |
|
|
Tensile Strength |
Yield Strength |
|
|
|
|
|
|
| Alloy |
UNS Designation |
Spec. |
psi |
MPa |
ksi |
psi |
MPa |
ksi |
Elongation in 2 in. (min.) % |
Grain Size Req. |
Max. Hardness |
Modulus of Elasticity (x106psi) |
Mean Coefficient of Thermal Expansion (IN./IN./°F x 10-6) |
Thermal Conductivity (BTU-in/ ft2-h-°F) |
| 600 |
N06600 |
B516, B517 |
80,000 |
550 |
80 |
35,000 |
240 |
35 |
30 |
— |
— |
30 |
6.9 |
103 |
Composition of Nickel Alloy 600 tubing and pipe
| Grade |
600 |
| UNS Designation |
N06600 |
| Nickel (Ni) |
72.0 Min. plus Cobalt |
| Chromium (Cr) |
14.00–17.00 |
| Iron (Fe) |
6.0–10.0 |
| Molybdenum (Mo) |
— |
| Titanium (Ti) Max. |
— |
| Aluminum (Al) Max. |
— |
| Cobalt (Co) Max. |
— |
| Tungsten (W) |
— |
| Vanadium (V) Max. |
— |
| Copper (Cu) Max. |
0.5 |
| Manganese (Mn) Max. |
1.0 |
| Niobium (Nb) plus Tantalum |
— |
| Carbon (C) Max. |
0.15 |
| Nitrogen (N) Max. |
— |
| Silicon (Si) Max. |
0.5 |
| Sulphur (S) Max. |
0.015 |
| Phosphorous (P) Max. |
— |
| Other Elements |
— |
Nickel Alloy 600 Product Range
| Alloy |
UNS Designation |
Werkstoff NR. |
Specifications* |
| 600 |
N06600 |
2.4816 |
B/SB516, B/SB517 |
*Note: The specifications noted including ASTM, ASME, or other applicable authorities are correct at the time of publication. Other specifications may apply for use of these materials in different applications.